Effect of Cold Working and Ring Indentation on Fatigue Life of Aluminum Alloy Specimens
2013
The article deals with the fatigue life of plates with hole made of aluminum alloy. Specifically, the combined effect of cold working expansion and ring indentation on improved fatigue life performance was investigated. Multiple fatigue tests were performed to determine the cycles to failure and the corresponding W¨ ohler diagram. Experimental results were compared with those of nontreated specimens. The conclusion was that cold working expansion and indentation create a delay on crack formation and fatigue failure.
Effect of residual stresses and their redistribution on the fatigue crack growth in cold-worked holes
2009
The cold-expansion process is widely used to enhance the fatigue life of structures with fastener holes. Various studies assert that the cold-expansion improves the fatigue strength of fastener holes; however, the improvement of fatigue life is difficult to quantify. The influence on fatigue life of cold-worked hole in a 6061-T6 alluminum allosy was studied by numerical and experimental tests. Fatigue crack growth tests were carried out to find the crack length and growth rates of crack propagating from hole edge. Thus, the cold-expansion process was modeled with a Lagrangian implicit code for metal forming to obtain the residual stress field. Progressive crack growth along the observed fat…